Abstract

BaAgBi was obtained as a by-product when Ba [rod, Alfa–Aesar (99.99%)], Ag [powder, −100 mesh, Alfa–Aesar (99.999%)], and Bi [powder, −100 mesh, Alfa–Aesar (99.999%)] were loaded into a tantalum tube (Nobel-Met. Ltd, >99.85%, 0.375 in. OD) in a 1:1:2 molar ratio in an Ar-filled glovebox. The tube was sealed in an arc-melter under argon, placed in a fused-silica jacket, and heated at 973 K for 3 days. The reaction container was cooled slowly to 673 K at 10 K h−1, and then quenched to room temperature. When the tantalum tube was opened in the Ar-filled glovebox, grey irregular-shaped crystals of BaAgBi were found in the product. Single crystals were mounted in 0.3 mm thin-walled capillaries for diffraction experiments.

Comments

This article is from Acta Crystallographica Section E 58 (2004): i21, doi:10.1107/S16005368020017. Posted with permission.

Copyright Owner

International Union of Crystallography

Share

COinS