Journal of Applied Physics
This study presents the effects of substitution of Zn 2+ for Co2+ at low concentrations and the effects of temperature variations on the structural, magnetic, and magnetostrictive properties ofcobalt ferrite. Although the Zn-substituted cobalt ferrite samples, Co1−x Zn xFe2O4 (x = 0.02, 0.04, 0.06, 0.09, and 0.17) did not show observable changes in crystal structure, the magnetic and magnetostrictive properties were strongly affected. The variation in magnetic susceptibilitywith composition can be related to the variations in magnetization, coercive field and magnetocrystalline anisotropy. The changes in coercive field were found to be primarily due to the variations in the magnetocrystalline anisotropy. The effect of magnetocrystalline anisotropyon magnetization was stronger at lower cation concentration than at higher concentrations. The decrease in magnetization around 150 K is attributed to the high magnetocrystalline anisotropyat low temperatures which prevented the maximum applied field of 4 MA/m from causing the saturation of magnetization in the samples. Because the magnetocrystalline anisotropy was determined with the magnetization data using the Law of Approach to saturation magnetization, the reliability of the result was found to decrease with decrease in temperature. Peak-to-peakmagnetostriction amplitude and the strain sensitivity decreased with increase in Znsubstitution.
Copyright 2013 American Institute of Physics. This article may be downloaded for personal use only. Any other use requires prior permission of the author and the American Institute of Physics.
American Institute of Physics
Nlebedim, Ikenna C.; Vinitha, M.; Praveen, P. J.; Das, D.; and Jiles, David C., "Temperature dependence of the structural, magnetic, and magnetostrictive properties of zinc-substituted cobalt ferrite" (2013). Electrical and Computer Engineering Publications. 23.