Description

A review is presented of work performed in our laboratory on the nondestructive inspection of metal matrix composites. In order to obtain damage representative of that which occurs in service, the specimens were mechanically loaded to intermediate load levels below that which causes final, catastrophic failure. Various nondestructive techniques were used both during and after the applied loadings to follow damage initiation and progress.

Book Title

Review of Progress in Quantitative Nondestructive Evaluation

Volume

2A

Chapter

Section 11: Metal Matrix Composites

Pages

729-746

DOI

10.1007/978-1-4613-3706-5_48

Language

en

File Format

application/pdf

Share

COinS
 
Jan 1st, 12:00 AM

Nondestructive Inspection and Evaluation of Metal Matrix Composites

La Jolla, CA

A review is presented of work performed in our laboratory on the nondestructive inspection of metal matrix composites. In order to obtain damage representative of that which occurs in service, the specimens were mechanically loaded to intermediate load levels below that which causes final, catastrophic failure. Various nondestructive techniques were used both during and after the applied loadings to follow damage initiation and progress.